Cold Bonded Wear Panels
YIHO Wear Panel solutions are ideal for a wide variety of mining, mineral processing and material handling for protection against extreme wear.
Application
Typical application examples:
· Chutes
· Cyclones
· Launders
· Pipes and tanks
· Conveyor transfer points
· Screen beams, underpans and components
· Vibratory feeders
Key features and benefits
· 92% Aluminium oxide material.
· Rubber compound blended with CN polymers.
· Buffed CN bonding layer and buffed edges.
· Manageable size and weight. Strip width 250mm makes it easy to install.
· Fire resistant and antistatic (FRAS) rubber compound available.
· Low sulphur rubber.
· Ceramic tiles bonded to rubber on all sides (except top surface).
· Supplied in square panels 500mm x 500mm.
· Extreme wear resistance.
· Outstanding adhesion to ceramic tiles, rubber and metal.
· For optimum cold vulcanised adhesion.
· Can be used in above and below ground applications.
· Stable rubber hardness with age.
· Resists tile cracking and pull out.
· Easy to install.
Rubber,Ceramic&Steel Specification
|
S.No. |
Material |
Attributes |
Properties |
| 1 |
Ceramic Tiles |
Material |
92%, 95%, T95%,99%, ZTA |
| 2 |
Rubber |
Component |
Natural rubber, nitrile-butadiene rubber ,Flame Retardant ,others |
|
Density |
~1.4g/cm3 |
||
|
Tensile strength at break |
≥10.6Mpa |
||
|
Elongation at break |
≥350% |
||
|
Shore Hardness |
45-65 |
||
|
Adhesive between tile and rubber |
≥3.8 Mpa |
||
|
Adhesive between rubber and equipment |
≥3.58Mpa |
||
|
Thermal conductivity.(normal temperature) |
2w/m·k |
||
|
Aging period |
≥15 Years |
||
|
Working temperature |
-50ºC - 200ºC |
||
| 3 |
Steel plate |
Material |
Q235A |
|
Density |
7.85g/cm3 |
||
|
Thickness |
3-10mm |
||
| 4 |
Adhesive |
Appearance |
Brown glutinous liquid |
|
Solid content |
20±3% |
||
|
Viscosity |
≥2.5 Mpa |
||
|
Peel strength |
48h N/2.5cm≥120 |
||
|
Compressive strength |
≥850 Mpa |
||
|
Working temperature |
-20ºC - 100ºC |